Manufacture and Characterization Physical and Mechanical Properties of Bioveneer Based Ark Clam Shells Composite

Authors

  • Evi Mariani M  Department of Physics, University of Sumatera Utara, Medan, Sumatera Utara, Indonesia
  • Kerista Tarigan  Department of Physics, University of Sumatera Utara, Medan, Sumatera Utara, Indonesia
  • Timbangen Sembiring  Department of Physics, University of Sumatera Utara, Medan, Sumatera Utara, Indonesia

DOI:

https://doi.org/10.32628/IJSRSET196326

Keywords:

Clam Shells Powder, Dental Veneer, Epoxy Resin, Hydroxyapatite

Abstract

Composite materials have been created for the applications of dental veneer from a mixture of raw materials : hydroxyapatite (HAp) powder from ark clam shells and epoxy resins by cold compression method with variations of composition hydroxyapatite (HAp) powder : epoxy resin (75 : 25)%wt, (80 : 20)%wt, (85 : 15)%wt, (90 : 10)%wt, dan (95 : 5)%wt. Sampling is created in three steps. The first step of ark clam shells powder is treated by smoothing it with a particle size of 200 mesh and heated at 900oC for 2 hours after it had been synthesized into hydroxyapatite (HAp) powder. The second step of the filler (hydroxyapatite powder) is mixed with dry mixing and then mixed with epoxy resin as a matrix. The third step of the homogeneous mixture is then inserted into the mold and compacted by heat to be more dense with pressure of 300 MPa or 3 ton held for 5 minutes at 27°C. The characterization results showed that the optimum composition of hydroxyapatite powder: epoxy resin (75 : 25)%wt with density value 0,1185 x 103 kg/m3, water absorption 1,163%, composed of -PO4 (phosphate), -CO3 (carbonate) and HOH groups. Mechanical properties with fracture strength 116 MPa, tensile strength 66,12 MPa, modulus of elasticity 3297,99 MPa and brinell hardness 75,87 HBR whose characterization results have met the conventional dental veneer standards.

References

  1. Belser UC, Magne P, Magne M. Ceramic laminate veneers: continuous evolution of indications. J Esthet Dent 1997;9:197–207
  2. K, Dahlan.2013. Potensi Kerang Darah sebagai Sumber Kalsium dalam Sintesis Biomaterial Substitusi Tulang.Departemen Fisika, Fakultas Matematika dan IPA, Institut Pertanian Bogor
  3. Barene A, Derchi G, Rossi A, Marconcini S. Longitudinal clinical evaluation of bonded composite inlay: A 3 year study. J Quintessence Int.2008;39(1): 65-67
  4. Prawesthi.2017. Case report: Labial Veneer all porcelain with press method for improving Aesthetic on patient with central diastema case. Jurnal Teknologi dan Seni Kesehatan. Vol. 08 No. 01, 2017 : 48 – 56
  5. Alothman, Youse, Maryam Saleh Bamasoud.2018. The Success of Dental Veneers According To Preparation Design and Material Type
  6. Gabby Ferdinandha.2011. Restorasi Estetik dan perbaikan posisi gigi dengan veneer labial menggunakan resin komposit secara direk
  7. Octariani, 2012.Pengaruh durasi sandblasting pada permukaan restorasi veneer resin komposit terhadap kuat rekat resin semen dengan email gigi
  8. Capa N, Ozkurt Z, Canpolat C, Kazazoghu E. Shear Bond strength of luting agent to fixed prosthodontic restorative core materials. Australian Dental Journal 2009; 54:334-340
  9. McCabe,F., Walls,WG.,2008, Applied Dental Materials. 9thed. Blackwell Publishing
  10. Eakle, Hatrick dan Bird. 2011, Dental Materials: Clinical Applications for Dental Assistants and Dental Hygienists, 2nd ed. Philadelpia: Elsevier
  11. Heyman, H.O., Indirect composit resin veneer: clinical technique and two year observation. J Quintessence Int 1987;18(2): 112-118
  12. Peumans M, Van Meerbeek B, Lambrechts P, Vanherle G. Porcelain veneers: a review of the literature. J Dent 2000;28:163–77.
  13. Chen JH, Shi CX, Wang M, Zhao SJ, Wang H. Clinical evaluation of 546 tetracycline-stained teeth treated with porcelain laminate veneers. J Dent 2005;33:3–8
  14. Broom,M.1985. The Biology and culture of marine BivalvaMollusc of the genus anadara.International centre for Living Aquatic Resources Management.Manila
  15. Heyman, H.O. Indirect composit resin veneer: clinical technique and two year observation. J Quintessence Int 1987;18(2): 112-118
  16. Alothman, Youse, Maryam Saleh Bamasoud.2018. The Success of Dental Veneers According To Preparation Design and Material Type.
  17. Manuel,Thomas S,K. David.2014. Importance of anatomic mock-up for predictable .
  18. Li et el. 2015. Recycling of shell wastes into nanosized calcium carbonate powders with different phase compositions. J. Clean. Prod. 92, 223e22
  19. Kilic, O., 2015. Cycle of limestone-lime and precipitated calcium carbonates. In: 12th Mining and Geotechnology Scientific Conference at “44. Jump over the Leather”, pp. 1e5. Ljubljana, Slovenia
  20. Guess PC, Stappert CF. Midterm results of a 5-year prospective clinical investigation of extended ceramic veneers. Dent Mater 2008;24:804–13.

International Journal of Scientific Research in Science, Engineering and Technology

Downloads

Published

2019-06-30

Issue

Volume 6, Issue 3, May-June-2019

Section

Research Articles

License

Copyright (c) IJSRSET

Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

How to Cite

[1]
Evi Mariani M, Kerista Tarigan, Timbangen Sembiring "Manufacture and Characterization Physical and Mechanical Properties of Bioveneer Based Ark Clam Shells Composite" International Journal of Scientific Research in Science, Engineering and Technology (IJSRSET), Print ISSN : 2395-1990, Online ISSN : 2394-4099, Volume 6, Issue 3, pp.132-140, May-June-2019. Available at doi : https://doi.org/10.32628/IJSRSET196326