Experimental Study on Geopolymer Motor with Marble Powder under High Temperature

Authors

  • Chintapalli Prasanthi  Civil Department, Jogaiah Institute of Technology & Science College Palakol , Andhrapradesh, India
  • T. Raja Sekhar   Civil Department, Jogaiah Institute of Technology & Science College Palakol , Andhrapradesh, India

Keywords:

Compressive Strength, Water Absorption, Dry Density.

Abstract

Geopolymers belong to a range of inorganic polymeric materials formed by activating silica aluminium rich minerals. Silica-aluminium rich industrial wastes etc. are activated with alkaline or alkaline-silicate solution at ambient or higher temperature to get Geopolymers. Geopolymerisation involves a number of processes such as dissolution, diffusion, polycondensation, and hardening. Optimization of such a complex system requires systematic study of several synthesizing parameters as well as of their interactions, which are extremely important issues for a geopolymer. Secondly, marble powder from different sources show different level of reactivity under specific geopolymer synthesis conditions and consequently affects the final properties. Hence, for manufacturing high performance geopolymer binder from marble powder, it is necessary to understand the effects of a various synthesis parameters and their relationship with mechanical properties and microstructure. The geopolymer mix composition is normally controlled by adjusting alkali and silicate content of activating solution. The SiO2 /Na2O ratio is an extremely important parameter which has major influence on physical and mechanical properties as well as on its microstructure. In the present study, an attempt has been made to study overall performance of geopolymer composites. Percentage of Na2O was taken 8 % and 10 %. SiO2 / Na2O ratio was varied from 1 to 1.6. Sand to marble powder ratio was kept 2:1, 1:1, and 1:2. Curing temperature and curing time were 800C and 72 hours respectively. After seven days, specimens were heated in Kiln at 2000C, 4000C, and 5500C for four hours and then kept in air for cooling. The effect of various synthesizing parameters at different temperature exposure on different properties such as Workability, Weight loss, Compressive strength, Sorptivity, Bulk density, Water absorption, Apparent porosity & Surface texture have been studied and the results were presented in the graphical and tabular form. It was observed that the geopolymer mortar is quite temperature resistant up to 5500C and remains dimensionally stable. However, some reduction in compressive strength was observed.

References

  1. Davidovits Joseph "Property of geopolymer cements" Geopolymer institute 02100 saint quintinfrance.
  2. Davidovits J. "Geopolymer inorganic materials new polymeric new materials" Geopolymer institute 02100 Saint Quentin, France in 1991.Journal of thermal analysis, vol. 37 pp 1633-1656(1991)
  3. Davidovits Joseph "Davidovits Geopolymer Institute, 30 Years of Successes and Failures in Geopolymer Applications" . Market Trends and Potential Breakthroughs.Geopolymer 2002 Conference, October 28-29, 2002, Melbourne, Australia.
  4. Palomo A. Grutzek M.W. Blanco M.T, "Alkali activated fly ash A cement for the future" Cement and Concrete Research 29 (1999) 1323-1329.
  5. Wallah S. E., Rangan B. V. "Low calcium fly ash base geopolymer concrete: long term property". Curtin University of Technology, G P O Box U 1987, Perth 6845, Western Australia, Australia.
  6. Malhotra, V. M. (1999). "Making Concrete "Greener" With Fly Ash." ACI Concrete International 21(5): 61-66.
  7. Davidovits Joseph "Geopolymers Man made Rock Geosynthesis and the resulting development of very high strength cement" Geopolymer Institute 02100 Saint-Quentin, France. Journal of materials education vol. 16 (2&3), pp 91-139 (1994)
  8. Van Jaarsveld J.G.S., van Deventer, J.S.J and Lukey G.C "The characterisation of source materials in fly ash-based geopolymers" Materials Letters 57 (2003) 1272-1280.Department of Chemical Engineering, the University of Melbourne, Victoria 3010, Australia.
  9. Van Jaarsveld, J. G. S., J. S. J. van Deventer, L. Lorenzen (1998). "Factors Affecting the Immobilization of Metals in Geopolymerized Fly Ash."
  10. Bakharev. T ""Geopolymeric materials prepared using class „F? fly ash and elevated temperature curing". Cement and Concrete Research 35 (2005) 1224-1232. Department of Civil Engineering, Monash University, Clayton, Victoria 3800, Australia.
  11. Raijiwala D.B., Patil H. S "Geopolymer concrete: A Concrete of next decade" Journal of Engineering Research and Studies. E-ISSN 0976-7916.
  12. HardjitoDjwantoro, Wallah Steenie E., SumajouwDody M. J., RanganB.Vijaya. "On the Development of Fly Ash-Based Geopolymer Concrete" ACI Materials Journals.Title no. 101-M52.
  13. HardjitoDjwantoro, Cheak Chua Chung, Lee Ing Carrie Ho, "Strength and Setting Times of Low Calcium Fly Ash-based Geopolymer Mortar" Vol 2, No 4 July 2008.

International Journal of Scientific Research in Science, Engineering and Technology

Downloads

Published

2017-06-30

Issue

Volume 3, Issue 3, May-June-2017

Section

Research Articles

License

Copyright (c) IJSRSET

Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

How to Cite

[1]
Chintapalli Prasanthi, T. Raja Sekhar , " Experimental Study on Geopolymer Motor with Marble Powder under High Temperature, International Journal of Scientific Research in Science, Engineering and Technology(IJSRSET), Print ISSN : 2395-1990, Online ISSN : 2394-4099, Volume 3, Issue 3, pp.249-254, May-June-2017.